Impurities: 0.01 (%) copper content: 98 (%) Name: bronze Size: 99 (Head) Origin: China Grade: C17200 softening temperature: 960 (℃) conductivity: ≥ 18 (% IACS) Hardness: 76 ( 38-44HRC) (HRB) Yield strength (0.2%) Mp: 1035 Tensile strength (Mpa): 1105 Thermal conductivity (W/m.k20 ℃: 105 Beryllium copper is a copper alloy excellent overall performance, versatile , but the price compared to other ordinary copper alloys to be expensive. Beryllium copper is a precipitation hardening alloy it is the mechanical properties, physical properties, chemical properties and good corrosion resistance combined with a unique non-ferrous alloys. beryllium copper alloy set fine The mechanical properties, physical properties and chemical properties in one, after heat treatment (solution treatment and aging treatment), the special steel with very high ultimate strength, elastic limit, yield strength and fatigue limit, but also have a high conductivity , thermal conductivity, high hardness, corrosion resistance, wear resistance, good casting properties, non-magnetic and shock characteristics of non-sparking, in the mold manufacturing, mechanical, electronics and other industries are widely used. features: no blisters, porosity, hardness balanced, compact, high strength, good thermal conductivity, good electrical conductivity, corrosion resistance, excellent wear resistance, good processability, high pressure conditions, stable performance, non-magnetic, excellent polishing performance, anti-adhesion properties. 2. Usage: high pressure injection molds and blow molds, mold inserts, rapid cooling, aluminum mold inserts to increase strength, abrasion resistance and shorten the molding cycle, hot runner nozzles, electrodes and punch materials , without magnetic mold, non-magnetic tools, high thermal conductivity bearing surface can be produced with high precision mirror. ● Chemical Composition: Beryllium Be :1.90-2 .15 Cobalt Co :0.35-0 .65 Ni Ni :0.20-0 .25 Copper Cu: Balance Si Si: <0.15 Iron Fe: <0.15 Al Al: <0.15 ● Mechanical Properties: Tensile strength (Mpa): 1105 specific gravity (g/cm3): 8.3 Yield Strength (0.2%) Mpa: 1035 softening temperature (℃): 930 Elongation (%): 1 Elastic Modulus (Gpa): 128 Hardness (HRC) :38-43 Thermal conductivity (W/m.k20 ℃): 105 Conductivity (IACS%) :18-48 Grade: C17200 / C17300 / C17000 copper alloy high strength deformed C17500 / C17510 deformation of high conductivity copper alloy wholesale factory specialized in producing beryllium copper (bronze) plates, rods, belt. specifications and diverse, many kinds of reliable quality, there is provided a single material welcome to contact us or online contact (Ali or QQ381003318).